PLA Premium 1.75mm Black Charcoal 500g
500g of PLA Premium 1.75mm Black Charcoal (RAL 9017)
Poids indiqué : quantité réelle de matière imprimable
Poids indiqué : quantité réelle de matière imprimable
13,00 € VAT inc.
10,83 € VAT exc.
10,83 € VAT exc.
Need some help to chose your filament? Take a look at this link "Everything about... THE FILAMENTS"
________________________
Our PLA Premium is a tough, easy to use high grade PLA type of filament, ideal for 3D printing. Slightly modified, the filament
retains the typical features of PLA, but makes it tougher and less brittle. Due to a low shrinkage factor our PLA Premium will not
deform after cooling. Poly Lactic Acid is a biodegradable plastic made from renewable natural resources and one of the
most popular materials for 3D printing.
Features:
• Tougher and less brittle compared to regular PLA
• Easy to print at low temperature
• Low warping
• Biodegradable
• Limited smell
________________________
Our PLA Premium is a tough, easy to use high grade PLA type of filament, ideal for 3D printing. Slightly modified, the filament
retains the typical features of PLA, but makes it tougher and less brittle. Due to a low shrinkage factor our PLA Premium will not
deform after cooling. Poly Lactic Acid is a biodegradable plastic made from renewable natural resources and one of the
most popular materials for 3D printing.
Features:
• Tougher and less brittle compared to regular PLA
• Easy to print at low temperature
• Low warping
• Biodegradable
• Limited smell
Size | Ø | Tolerance Roundness |
---|---|---|
1,75mm | ± 0,05mm | ≥ 95% |
2,85mm | ± 0,10mm | ≥ 95% |
Description | Testmethod | Typical value |
---|---|---|
Specific gravity | ASTM D1505 | 1,24 g/cc |
MFI | - | 6,0 g/10 min |
Tensile strength | ASTM D882 | 110 MPa (MD) 145 MPa (TD) |
Elongation at break | ASTM D882 | 160% (MD) 100% (TD) |
Tensile modulus | ASTM D882 | 3310 MPa (MD) 3860 Mpa (TD) |
Impact Strength | - | 7,5 KJ/m² |
Description | Testmethod | Typical value |
---|---|---|
Printing temperature | - | 180-210°C |
Melting temperature | - | 210°C ± 10°C |
Melting point | ASTM D3418 | 145-160°C |
vicat softening temperature | ISO 306 | ± 60°C |