  • PolyMide PA6-GF 1.75mm 500g Grey, Polymaker

PolyMide PA6-GF 1.75mm 500g Grey, Polymaker

PolyMide PA6-GF 1.75mm 500g Grey
Indicated wieght: actual amount of printable material.
53,99 € VAT inc.
44,99 € VAT exc.
To prevent automated spam submissions leave this field empty.
PolyMide™ is a family of Nylon/polyamide based filaments. Produced with Polymaker’s Warp-Free™ technology, PolyMide™ filaments deliver engineering properties intrinsic to Nylon and ease of printing.

PolyMide™ PA6-GF is a glass fiber reinforced PA6 (Nylon 6) filament. The material exhibits excellent thermal and mechanical properties without sacrificing the layer adhesion.

Specifications:
Recommended settings Mechanical properties Thermal properties Notes
Printing temp.: 280-300°C Young's modulus: 4431±184 (MPa) Heat deflection temperature (ISO 75 1.8 MPa): 157°C Drying Settings:
80˚C for 12h
Printing speed: 60mm/s Tensile strength: 84.5±2.1 (MPa) Heat Deflection Temperature
(ISO 75 0.45 MPa):
191 ˚C
Recommended Support Materials:
BVOH
Bed temp.: 25-50°C (do NOT exceed 50°C) Bending strength: 136.4±1.6 (MPa) Melting Temperature:
215 (°C)
Other:
Annealing 80℃ 6h
Bed surface: almost any surface with a thin coat of 3DLac Charpy impact strength: 16.5±0.5 (kJ/m²)    
Fan: OFF      

We highly recommend to use a wear resistant nozzle.

PolyMide™ PA6 GF features Polymaker's Warp-Free™ technology and Fiber Adhesion™ technology:

Warp-Free™ technology enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.

Fiber Adhesion™ technology improves the layer adhesion of fiber reinforced materials, by optimizing the surface chemistry of the fibers to achieve better dispersion and bonding to the matrix. This results in better strength along the Z-axis and reduced mechanical anisotropy.
Share